Rilsan? HT CESV P010 TL
聚二甲苯酰胺
Arkema
产品说明：
Rilsan ? HT CESV P010 TL is a flexible polyphthalamide produced from a renewable source, typically used to replace metal in tubing for high-temperature automotive, transportation and other demanding technical applications.
MAIN APPLICATIONS
Thermoplastic lines for automotive & transportation applications such as high temperature air/vacuum, aggressive media and oil management systems, cooling and selective catalyst reduction lines, etc.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 密度 | 1.02 | g/cm? | *** 1183 |
| 溶化体积流率（MVR） |
|
| *** 1133 |
| 300°C/2.16 kg | 0.500 | cm?/10min | *** 1133 |
| 300°C/5.0 kg | 3.10 | cm?/10min | *** 1133 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 肖氏硬度 |
|
| *** 868 |
| 邵氏 D | 74 |
| *** 868 |
| 邵氏 D, 15 秒 | 64 |
| *** 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量 | 880 | MPa | *** 527-2 |
| 拉伸应力 (断裂) | 41.0 | MPa | *** 527-2 |
| 拉伸应变 (断裂) | > 130 | % | *** 527-2 |
| 弯曲模量 | 820 | MPa | *** 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 简支梁缺口冲击强度 |
|
| *** 179 |
| -40°C | 14 | kJ/m? | *** 179 |
| 23°C | 76 | kJ/m? | *** 179 |
| 简支梁无缺口冲击强度 |
|
| *** 179 |
| -30°C | 无断裂 |
| *** 179 |
| 23°C | 无断裂 |
| *** 179 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 熔融温度 | 255 | °C | *** 11357-3 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|
| Hoop Stress |
|
|
|
| 23°C | 30.0 | MPa |
|
| 150°C | 5.00 | MPa |
|
| Renewable Carbon Conent | > 45 | % | ASTM D6866 |
| 挤出 | 额定值 | 单位制 |
|
|---|
| 干燥温度 | 100 到 110 | °C |
|
| 干燥时间 | 4.0 到 8.0 | hr |
|
| 熔体温度 | 270 到 300 | °C |
|